CoCr Milling Discs
Starbond Easy Disc
CoCrW milling disc outstanding for manufacturing of crowns, bridges, frameworks, telescopes, bars, attachments and implant-supported superstructures. Starbond Easy Disc is based on a proven veneering alloy already used in conventional casting technique. Free of nickel, lead, beryllium and cadmium. Type 4 pursuant to DIN EN ISO 22674.
Advantages for users:
- Medium hardness of 289 HV 10
- Excellent metal-ceramic Bonding
- Biocompatible
- Easy polishing
- Laser weldable
- Dry and wet milling
Composition in percent by mass:
| Co |
61% |
| Cr |
27.5% |
| W |
8.5% |
| Si |
1.6% |
| C,Mn,Fe |
<1% |
Technical properties:
| Proof stress (Rp 0.2) |
416MPa |
| Ultimate tensile strength |
663MPa |
| Elongation |
18% |
| Elastic modulus |
191GPa |
| Vickers hardness |
289HV10 |
| Density |
8.6g/cm³ |
| CTE (20-500°C) |
14.3 x 10⁻⁶K⁻¹ |
| CTE (20-600°C) |
14.6 x 10⁻⁶K⁻¹ |
| Laser weldable |
Yes |
| Type (DIN EN ISO 22674) |
4 |
Sizes:
| 08mm x 98.3mm |
with edge |
Ref. 140508 |
| 10mm x 98.3mm |
with edge |
Ref. 140510 |
| 12mm x 98.3mm |
with edge |
Ref. 140512 |
| 13.5mm x 98.3mm |
with edge |
Ref. 140513 |
| 15mm x 98.3mm |
with edge |
Ref. 140515 |
| 16mm x 98.3mm |
with edge |
Ref. 140516 |
| 18mm x 98.3mm |
with edge |
Ref. 140518 |
| 20mm x 98.3mm |
with edge |
Ref. 140520 |
| 25mm x 98.3mm |
with edge |
Ref. 140525 |
| 30mm x 98.3mm |
with edge |
Ref. 140530 |
| 08mm x 99.5mm |
without edge |
Ref. 140008 |
| 10mm x 99.5mm |
without edge |
Ref. 140010 |
| 12mm x 99.5mm |
without edge |
Ref. 140012 |
| 14mm x 99.5mm |
without edge |
Ref. 140014 |
| 15mm x 99.5mm |
without edge |
Ref. 140015 |
| 16mm x 99.5mm |
without edge |
Ref. 140016 |
| 18mm x 99.5mm |
without edge |
Ref. 140018 |
| 20mm x 99.5mm |
without edge |
Ref. 140020 |
| 25mm x 99.5mm |
without edge |
Ref. 140025 |
| 30mm x 99.5mm |
without edge |
Ref. 140030 |
HOTLINE: 