CoCr Milling Discs
MoguCera C Disc
CoCrMo milling disc with excellent properties for the manufacture of crowns, bridges, frameworks, telescopes, bars, attachments and implant supported superstructures. MoguCera C Disc is based on a non-precious ceramic alloy already used in the conventional casting technology. Free of nickel, beryllium, lead und cadmium. Type 4 pursuant to DIN EN ISO 22674 with a very wide range of indications.
Advantages for users:
- Medium hardness of 288 HV 10
- Excellent metal-ceramic Bonding
- Biocompatible
- Easy to work with and very to polish
- Laser weldable
- Suitable for dry and wet milling
Composition in percent by mass:
| Co |
65% |
| Cr |
28% |
| Mo |
5% |
| C,Si,Nb,Mn,Fe |
<1% |
Technical properties:
| Proof stress (Rp 0.2) |
413MPa |
| Ultimate tensile strength |
597MPa |
| Elongation |
12% |
| Elastic modulus |
206GPa |
| Vickers hardness |
288HV10 |
| Density |
8.3g/cm³ |
| CTE (20-500°C) |
14.5 x 10⁻⁶K⁻¹ |
| CTE (20-600°C) |
14.8 x 10⁻⁶K⁻¹ |
| Laser weldable |
Yes |
| Type (DIN EN ISO 22674) |
4 |
Sizes:
| 08mm x 98.3mm |
with edge |
Ref. 138108 |
| 10mm x 98.3mm |
with edge |
Ref. 138110 |
| 12mm x 98.3mm |
with edge |
Ref. 138112 |
| 13.5mm x 98.3mm |
with edge |
Ref. 138113 |
| 15mm x 98.3mm |
with edge |
Ref. 138115 |
| 16mm x 98.3mm |
with edge |
Ref. 138116 |
| 18mm x 98.3mm |
with edge |
Ref. 138118 |
| 20mm x 98.3mm |
with edge |
Ref. 138120 |
| 25mm x 98.3mm |
with edge |
Ref. 138125 |
| 30mm x 98.3mm |
with edge |
Ref. 138130 |
| 08mm x 99.5mm |
without edge |
Ref. 138008 |
| 10mm x 99.5mm |
without edge |
Ref. 138010 |
| 12mm x 99.5mm |
without edge |
Ref. 138012 |
| 14mm x 99.5mm |
without edge |
Ref. 138013 |
| 15mm x 99.5mm |
without edge |
Ref. 138015 |
| 16mm x 99.5mm |
without edge |
Ref. 138016 |
| 18mm x 99.5mm |
without edge |
Ref. 138018 |
| 20mm x 99.5mm |
without edge |
Ref. 138020 |
| 25mm x 99.5mm |
without edge |
Ref. 138025 |
| 30mm x 99.5mm |
without edge |
Ref. 138030 |
HOTLINE: 