NPM-Alloys for Partial Dentures
MoguCast EH
CoCr partial denture alloy for sophisticated combined restorations. Free of nickel, beryllium, lead and cadmium. Type 5 pursuant to DIN EN ISO 22674.
- Excellent degree of purity
- Biocompatible and extremly corrosion resistant
- High wearing comfort due to low thermal conductivity
- Spring hard
Advantages for dental technicians:
- Particularly suitable for extremely graceful removables
- Ideal alloy for restorations which are exposed to very high loads
- Excellent for casting of 3D printed plastic parts
- Universally applicable for clasp-retained prostheses and combined techniques
- Pleasant polishing properties and easy finishing
- Optimal conditions for laser welding
- System-free working due to very good alloy properties
Composition:
| Co |
62% |
| Cr |
25% |
| W |
9% |
| Nb |
2% |
| C,V,Mo,Mn,Si |
<1% |
Technical properties:
| Proof stress (Rp 0.2) |
662MPa |
| Ultimate tensile strength |
877MPa |
| Elongation |
>4% |
| Elastic modulus |
200 - 210GPa |
| Vickers hardness |
420 HV 10 |
| Density |
8.7g/cm³ |
| Melting range |
1320 - 1400°C |
| Preheating temperature |
850 - 950°C |
| Casting temperature |
1500 - 1550°C |
| Laser weldable |
Yes |
| Type (DIN EN ISO 22674) |
5 |